103 Clay
Low fire plastic terra cotta body designed
for the classroom. Traditional terra cotta
color at cones 06 oxidation. Deeper brick
red at cone 2.
Shrinkage: 9% at C/06, 14% at C/2
Absorption: 12% at C/06, 6% at C/2
Arcilla de Color Barro de baja temperatura diseñada para las escuelas. Color Barro tradicional quemada a cono 06 en horno de gas. Color Barro mas oscuro quemado en cono 2.
Contraccion: 9 % a C/06, 14% a C/2.
Absorcion: 12% a C/06, 6% a C/2.
DISCOUNTS FOR LARGE QUANTITIES AVAILABLE / DESCUENTOS EN CANTIDADES GRANDES DISPONIBLE
We can deliver to any freight forwarder in Miami / Le podemos entregar a su adjente aduanero en Miami
_____________________________________________________________________
104 Clay
Versatile clay containing fine grog. Good for
hand building, slab work and throwing.
Shrinkage: 6% at C/06, 11% at C/4
Absorption: 13.2% at C/06, 3% at C/4
Arcilla color barro con chamota fina. Buena para moldeo a mano, trabajo a rodillo o en un torno.
Contraccion: 6% a C/06, 11% a C/4
Absorbcion: 13.2% a C/06, 3% a C/4
__________________________________________________________
105 Clay
Shrinkage: 6% at C/06, 6.5% at C/04
Absorption: 15.5% at C/06, 14.5% at C/04
Contraccion: 6% a C/06, 6.5% a C/04
Abosorbcion: 15.5% a C/06, 14.5% a C/04
_________________________________________________________
105G (With Grog)
Same as 105 with the addition of fine grog. Gives a toothy clay that many potters prefer. Suggested bisque temperature cone 04.
Shrinkage: 5.6% at C/06, 5.0% at C/04
Absorption: 15.3% at C/06, 14.5% at C/04
Arcilla igual que la 105 con la addicion de chamota fina. Una arcilla preferida por los escultores y alfareros. Es tambien una arcilla muy buena para crear losas y piezas grandes. Recomendamos biscochar a cono 04.
Contraccion: 5.6% a C/06, 5.6% a C/04
Absorbcion: 15.3% a C/06, 14.5% a C/04
_________________________________________________________
112 Clay
Plastic clay for wheel and modeling. The addition of granular manganese gives a speckled
surface. The ideal temperature for developing best color tone is cone 5. Good results may
be expected in reduction or exidation firing. Suggested bisque temperature cone o4.
Shrinkage: 12% at C/4, 12.5% at C/6.
Absorption: 4.5% at C/4, 2.5% at C/6.
Arcilla bien plastica para el torno y modelar. La adicion de manganese granular le da una apariencia moteado en la superficie. La temperatura ideal para desarrollar el mejor tono de color en cono 5. Buenos resultados pueden ser esperado en reduccion o oxidacion. Sujerimos biscochar a cono 04.
Contraccion: 12% a C/4, 12.5% a C/6.
Absorbcion: 4.5% a C/4, 2.5% a C/6
_____________________________________________________
211 Clay
HAZELNUT BROWN CLAY - Cone 4-6 (Photo C/6)
A nice plastic clay for throwing and handbuilding. At C/6 oxidation, its a warm brown color usually associated with reduction firing. Reacts well with glazes. Suggested bisque temperature
C/04. Shrinkage: 13% at C/6. Absorption: 2.25% at C/6.
ARCILLA BROWN DE AVELLANA - Cono 4-6 (Foto C / 6)
Una arcilla plástica agradable para lanzar y handbuilding. En la oxidación C / 6, es un color marrón cálido usualmente asociado con el disparo de reducción. Reacciona bien con esmaltes. Temperatura de bisque sugerida C / 04.
Contracción: 13% en C / 6. Absorción: 2,25% en C / 6.
___________________________________________________
213 Clay
A white body formulated for cone 6 firing. Plastic, throwable clay. Suggested bisque temperature cone 04.
Shrinkage: 12% at cone 6
Absorption: 1.7% at C/6
Arcilla blanca formulada para quemar a cono 6. Bien plastica y buena utilizar en el torno. Temperatura de biscocho recomendada cono 04.
Contraccion: 12% a C/6
Absorbcion: 1.7% a C/6
______________________________________________________
225 Clay
C/4-6
Same as clay 112 but without the manganese specks. Ideal for wheel and slab work.
Cone 4 Average Shrinkage 12.0% Absorption 4.5%
Cone 6 Average Shrinkage 12.5% Absorption 2.5%
Igual que la arcilla 112 pero sin las motas de manganeso. Ideal para trabajos con ruedas y losas.
Cono 4 Contracción promedio 12,0 % Absorción 4,5 %
Cono 6 Contracción media 12,5 % Absorción 2,5 %
____________________________________________________________
240 Clay
A very smooth, plastic throwing body.
Shrinkage: 13% at C/6.
Absorption: 2.75% at C/6
Una arcilla bien suave y lisa bien plastica para uso en torno.
Contraccion: 13% a C/6
Absorbcion: 2.75% a C/6
_________________________________________________________
266 Clay
Dark Brown Clay Cone 4-5. Gives reduction-like dark brown color in electric kiln.
Smooth and plastic. Good for all techniques. Suggested bisque Temperature C/04.
Shrinkage: 11.5% at C/4, 13% at C/6.
Absorption: 2.4% at C/4, 1.4% at C/6.
Arcilla Marron Oscura, Cono 4-5. A reduccion color marron oscuro en horno electrico. Esta es suave y plastica al tocar, muy buena para todas las technicas. Sugerimos biscochar a cono 04.
Contraccion: 11.5% a C/4, 13% a C/6.
Absorbcion: 2.4% a C/4, 1.4% a C/6.
_______________________________________________________
#11 White Stoneware Clay
The No.11 White Stoneware is an off-white plastic clay that is formulated to be versatile and strong. It is ideal for throwing and all types of handbuilding. The greenware is very strong and maintains that strength after firing. The low iron content is well suited for limiting the amount of interaction with the glaze surface.
Cone 5:
Shrinkage: 11.2%
Absorption: 7.03%
Cone 10:
Shrinkage: 12.9%
Absorption: 1.6%
El gres blanco No.11 es una arcilla plástica blanquecina formulada para ser versátil y resistente. Es ideal para lanzar y todo tipo de construcción manual. El greenware es muy fuerte y mantiene esa fuerza después de la cocción. El bajo contenido de hierro es muy adecuado para limitar la cantidad de interacción con la superficie del esmalte.
Cono 5:
Contracción: 11,2%
Absorción: 7,03%
Cono 10:
Contracción: 12,9%
Absorción: 1,6%
__________________________________________________________
PM-BLACK EARTHENWARE LOW FIRE CLAY
Black earthenware clay body. Its black color in oxidizing atmosphere is a highlight in the range of low firing colors. Its fineness and plasticity make it an excellent choice for throwing and modelling. Very good with standard pottery glazes. Available in extruded body (moist form), being suitable for wheel-throwing, shaping and modeling.
Firing range: Cone 06-05 (1855º-1911ºF)
Water content: 21%
Plasticity (IP Atterberg): 16
Carbonate content (CaCO3): 8%
Drying shrinkage: 5.0%
Firing shrinkage at Cone 06: 0.9%
Porosity (water absorption) at Cone 06: 14.3%
Dry bending strength: 4.5 N/mm2
Fired bending strength at Cone 06: 28.9 N/mm2
Thermal coefficient (a25-500ºC): 77.9x10-7ºC-1
Cuerpo de barro loza negra. Su color negro en atmósfera oxidante destaca en la gama de colores de baja cocción. Su finura y plasticidad lo convierten en una excelente opción para lanzar y modelar. Muy bueno con esmaltes de cerámica estándar. Disponible en cuerpo extruido (forma húmeda), siendo apto para moldear, moldear y modelar.
Campo de tiro: Cono 06-05 (1855º-1911ºF)
Contenido de agua: 21%
Plasticidad (IP Atterberg): 16
Contenido de carbonato (CaCO3): 8%
Contracción por secado: 5,0%
Contracción por cocción en el Cono 06: 0,9%
Porosidad (absorción de agua) en el Cono 06: 14,3%
Resistencia a la flexión en seco: 4,5 N/mm2
Resistencia a la flexión al fuego en el Cono 06: 28,9 N/mm2
Coeficiente térmico (a25-500ºC): 77,9x10-7ºC-1
____________________________________
ANETO CLAY
Aneto is translucent white porcelain body which stands out for its high plasticity, and makes it exceptional for wheel-throwing and modeling. Its formula is very stable and provides a secure firing range between Cone 6 and Cone 8. Available in extruded body (moist form). Supplied in a practical 5 kg cylindrical format with double packaging.
Firing range: Cone 6-8 (2269º-2320ºF)
Biscuit: Cone 06 (1855ºF)
Water content: 21%
Plasticity (IP Atterberg): 11
Carbonate content (CaCO3): 0%
Drying shrinkage: 4.0%
Firing shrinkage at Cone 7: 9.8%
Porosity (water absorption) at Cone 7: 0.0%
Dry bending strength: 3.1 N/mm2
Fired bending strength at Cone 7: 45.2 N/mm2
Thermal coefficient (a25-500ºC): 59.2x10-7ºC-1
Aneto es una pasta porcelánica blanca translúcida que destaca por su alta plasticidad, lo que la hace excepcional para el torno y el modelado. Su fórmula es muy estable y proporciona un rango de disparo seguro entre el Cono 6 y el Cono 8. Disponible en cuerpo extruido (forma húmeda). Se suministra en un práctico formato cilíndrico de 5 kg con doble embalaje.
Campo de tiro: Cono 6-8 (2269º-2320ºF)
Galleta: Cono 06 (1855ºF)
Contenido de agua: 21%
Plasticidad (IP Atterberg): 11
Contenido de carbonato (CaCO3): 0%
Contracción por secado: 4,0%
Contracción por cocción en el Cono 7: 9,8%
Porosidad (absorción de agua) en el Cono 7: 0,0%
Resistencia a la flexión en seco: 3,1 N/mm2
Resistencia a la flexión al fuego en el Cono 7: 45,2 N/mm2
Coeficiente térmico (a25-500ºC): 59,2x10-7ºC-1
DISCOUNTS FOR LARGE QUANTITIES AVAILABLE / DESCUENTOS EN CANTIDADES GRANDES DISPONIBLE
We can deliver to any freight forwarder in Miami / Le podemos entregar a su adjente aduanero en Miami
Item will usually ship within 1-2 business days.